This title is printed to order. This book may have been self-published. If so, we cannot guarantee the quality of the content. In the main most books will have gone through the editing process however some may not. We therefore suggest that you be aware of this before ordering this book. If in doubt check either the author or publisher’s details as we are unable to accept any returns unless they are faulty. Please contact us if you have any questions.
Wahrend der magnetokalorische Effekt (MKE) bei den ferroma- gnetischen Metallen der 1. langen Periode ausgiebig untersucht wurde (1,2), liegen u.W. keine entsprechenden Ergebnisse fur antiferromagnetische Legierungen dieser Metalle vor. Wie eine thermodynamische Betrachtung (3) zeigt, ist die Groesse des MKE proportional zur Messtemperatur T und zur Temperaturabhangig- keit der magnetischen Suszeptibilitat X (bei T) und umgekehrt proportional zur spezifischen Warme c (bei T). Im folgenden soll uber Messungen von X (T) und des MKE bei drei antiferro- magnetischen Substanzen berichtet werden: 1) Eisen-Mangan-Legierungen in dem Bereich (40 at%
$9.00 standard shipping within Australia
FREE standard shipping within Australia for orders over $100.00
Express & International shipping calculated at checkout
This title is printed to order. This book may have been self-published. If so, we cannot guarantee the quality of the content. In the main most books will have gone through the editing process however some may not. We therefore suggest that you be aware of this before ordering this book. If in doubt check either the author or publisher’s details as we are unable to accept any returns unless they are faulty. Please contact us if you have any questions.
Wahrend der magnetokalorische Effekt (MKE) bei den ferroma- gnetischen Metallen der 1. langen Periode ausgiebig untersucht wurde (1,2), liegen u.W. keine entsprechenden Ergebnisse fur antiferromagnetische Legierungen dieser Metalle vor. Wie eine thermodynamische Betrachtung (3) zeigt, ist die Groesse des MKE proportional zur Messtemperatur T und zur Temperaturabhangig- keit der magnetischen Suszeptibilitat X (bei T) und umgekehrt proportional zur spezifischen Warme c (bei T). Im folgenden soll uber Messungen von X (T) und des MKE bei drei antiferro- magnetischen Substanzen berichtet werden: 1) Eisen-Mangan-Legierungen in dem Bereich (40 at%