This title is printed to order. This book may have been self-published. If so, we cannot guarantee the quality of the content. In the main most books will have gone through the editing process however some may not. We therefore suggest that you be aware of this before ordering this book. If in doubt check either the author or publisher’s details as we are unable to accept any returns unless they are faulty. Please contact us if you have any questions.
brittle fracture; property degradation; mechanical properties; failure analysis; 55NiCrMoV7; corrosion; cable wires; hydrogen-induced cracking; hierarchical Bayesian inference; correlation model; maintenance interventions; HSLA steel; API X52; gas pipeline; microstructure; neutron diffraction; strength; stress corrosion cracking; atmospheric corrosion; weathering steel; experimental tests; corrosion losses; deposition rate of chlorides; fracture resistance; Charpy impact test; J-R curve; dislocation; precipitate; high-strength X80 steel; buried pipeline; strike-slip fault; strain-based design; compressive strain capacity; local buckling; finite element method; stress corrosion cracking; localized corrosion; pre-stressed concrete; hydrogen embrittlement; API X80 steel; strain-hardening exponent; high-frequency hot-induction bending; thermal treatments; steel; fracture mechanics; tensile test; cohesive zone model; internal damage; XRCT; Ferrite-martensite dual-phase (FMDP) steel; dynamic tensile testing; dislocation multiplication; adiabatic heating; failure mechanism; dual phase steel; annealing; volume fraction of secondary phase; grain size; strain-hardening exponent; yield strength; ultimate tensile strength; properties prediction; combined defect; gas pipeline; mechanical damage; failure pressure; finite element method; low-cycle fatigue; cyclic behaviour; strain energy density; bainite; carbide; n/a